Effect of Sandpaper Meshes on the Performance of Tilia Sp. Self-Repairing Coatings.

This study aimed to investigate the impact of different sandpaper sanding meshes on the mechanical and optical properties of microencapsulated Tilia sp. film. An orthogonal experiment revealed that sanding between primers had the most significant effect. Furthermore, an independent experiment implied that increasing the mesh size resulted in decreased surface roughness and decreased color difference, elongation at break, and gloss after liquid resistance. In the aging test, the color difference of the paint film increased with the aging time, and the gloss tended to stabilize. Additionally, the anti-aging gloss of 240 mesh sandpaper used between primers remained relatively stable. The paint film sanded with 240 mesh sandpaper between primers displayed small and regular cracks after temperature and UV aging. Overall, the paint film demonstrated good comprehensive performance when sanded with 240 mesh between primers, 240 mesh between primer/topcoat, and 1000 mesh for topcoat. Self-repairing microcapsules showed better repair efficacy on the coating. This study provides a technical reference for the development of self-repairing coatings.

Effect of Coating Process on Mechanical, Optical, and Self-Healing Properties of Waterborne Coating on Basswood Surface with MF-Coated Shellac Core Microcapsule.

Self-repairing microcapsules prepared with melamine formaldehyde (MF) resin as wall material and shellac and waterborne coating as core material were added to waterborne coating to prepare a self-repairing coating. In order to explore the effect of the coating process on the performance of the waterborne coating on the basswood surface with microcapsules, the number of coating layers of primer and finish and the addition mode of the microcapsules were tested as influencing factors. The effects of different coating processes on the optical, mechanical, and liquid resistance of the basswood surface coating were investigated. The results showed that different coating processes had little effect on the color difference of the coating. When the coating process was two layers of primer and three layers of finish, and microcapsules were added to the finish, the minimum gloss of the basswood surface coating at 60° incident angle was 10.2%, and the best mechanical properties, liquid resistance, and comprehensive properties were achieved. Finally, the aging resistance and self-healing performance of the waterborne coating on the basswood surface prepared by this coating process were explored. The results showed that the waterborne coating had a certain repair effect on scratch damage. This paper lays a theoretical foundation for the practical application of self-healing microcapsules in wood-surface waterborne coatings.

Effect of Concentration of Thermochromic Ink on Performance of Waterborne Finish Films for the Surface of Cunninghamia Lanceolata.

Using Cunninghamia lanceolata as a substrate, the thermochromic ink was added to the waterborne finish to test the optical properties and mechanical properties of the finish film. The results showed that the discoloration performance of the finish film with 15.0% and 30.0% of the thermochromic ink was better. The gloss of the finish film changes irregularly when the concentration increases. The finish film with a thermochromic ink concentration of 10.0% has the highest gloss, and with a concentration of 30.0% has the lowest gloss. When the thermochromic ink concentration exceeds 15.0%, the impact resistance of the finish film is slightly enhanced. The concentration is not related to the liquid resistance of the finish film. When the thermochromic ink concentration was 0-15.0%, the particle distribution uniform reunion was not much. The discoloration mechanism of discolored finish film can be considered to be as follows. After adding thermochromic ink, when the finish film temperature rises, it fades from red to colorless. When the temperature is lowered, the thermochromic ink changes to its original colour again, and the thermochromic effect is stable and sustainable. On the basis of the above results, when the thermochromic ink concentration is 15.0%, the general performance of the waterborne finish film on the Cunninghamia lanceolata surface is the best. This study provides new prospects in using thermochromic ink for waterborne finish film.

The Effect of Glass Fiber Powder on the Properties of Waterborne Coatings with Thermochromic Ink on a Chinese Fir Surface.

In this study, the effect of glass fiber powder on the properties of waterborne coatings with thermochromic ink was investigated, using Chinese fir board as the base material and temperature-sensitive thermochromic waterborne coatings with thermochromic ink as the paint base. The concentration of glass fiber powder was determined when the microstructure, optical properties, mechanical properties, liquid resistance, and heat preservation effect were the best. The results showed that the paint film with glass fiber powder concentration of 1.0% to 7.0% had better discoloration performance. With an increase of the glass fiber powder concentration, the gloss of the paint film decreased gradually, and when the concentration of glass fiber powder was 0% to 5.0%, the gloss of the paint film was better. The concentration of glass fiber powder had no effect on the adhesion, impact resistance, and liquid resistance. In the first 2.5 min, the temperature value of the waterborne coating with 3.0% glass fiber powder was higher than that without glass fiber powder, which has a certain heat preservation effect. When the glass fiber powder content was 3.0%, the microstructure of paint film was the best. The composition of paint film with different glass fiber powder concentrations was not different and the discoloration performance of paint film with heat preservation effect was not affected by time. The analysis showed that the waterborne coating with 3.0% glass fiber powder had the best comprehensive performance. This work provides a technical reference for the industrialization of heat preservation and thermochromic coating on wood.